We are highly engaged in the business of manufacturing and supplying a qualitative range of Glass Epoxy Sheet for our customers. It is manufactured from the premium grade glass material under guidance of our experienced professionals who ensure its flawless finishing and unmatched quality. I has superior strength and highly resistant to chemicals. Apart from this, it is quality certified by our experts after testing it on various parameters. This product is available for sale as per requirements at reasonable rates.
Glass Epoxy Sheet Property Data :
Technical Data | Method of Verification | Unit | 3240 |
I.Physical Properties | | | |
Density | ISO 1183 | g/cm3 | 2.0~2.1 |
Water absorption 24hrs | ISO 62 | % | 0.05~0.15 |
III.Thermal Properties | | | |
Max. service temperature -Short term | ISO 75-2 | C | / |
Max. service temperature - Long term | ISO 75-2 | C | 130~140 |
Coefficient of Thermal Expansion-LW | ISO 11359 | m/K | / |
Coefficient of Thermal Expansion-CW | ISO 11359 | m/K | / |
Thermal Conductivity | ISO 11359 | W/(mK) | 2.2~2.5 |
Flammability | UL 94 | Class | V-1 |
II.Mechanical Properties |
|
|
|
Tensile strength at yield | ISO 527-2 | MPa | 220 |
Tensile strength at break | ISO 527-2 | Mpa | / |
Hardness Rockwell | DIN 53505 |
| 120-125 |
Izod impact strength | ISO 179 | kJ/m2 | 33 |
Bending Strength | ISO 527-2 | Mpa | / |
Flexural strength-LW | ISO 179 | Mpa | 314 |
Flexural strength-CW | ISO 179 | Mpa | 216 |
Adhesive Strength | ISO 179 | N | 5600 |
Compression strength-LW | ISO 179 | Mpa | 350 |
Compression strength-CW | ISO 179 | Mpa | 147 |
IV.Electrical Properties | | | |
Volume resistively | IEC 60093 | Ohm () * cm | 1.3x1014 |
Surface resisively | IEC 60093 | Ohm () | 3.5x1012 |
Electric strength- LW | VDE 0303 | kV/mm | 14.2 |
Breakdown Voltage-CW | VDE 0303 | kV | >34 |
Relative dielectric coefficient | VDE 0303 | / | 4.7 |
Dielectric Loss mudule | VDE 0303 | 50HZ | 0.04 |
Arc resistance | VDE 0303 | S | / |
NOTE : 1 g/cm3 = 1,000 kg/m3, 1 Mpa = 1 N/mm2, 1kV/mm = 1 MV/m
Additional Information :